ZHANG Lei1,2, ZHANG Xuefeng2, ZHAO Chaoyong2, CHEN Min2
(1. School of Materials Science and Engineering, Xihua University, Chengdu 610039, China;2. College of Vanadium and Titanium, Panzhihua University, Panzhihua 617000, China)
Abstract: The development history, luminescence mechanism and the main preparation methods, such as high temperature solid-state reaction process, hydrothermal method, sol-gel method, combustion method, of vanadate phosphors were reviewed. The research progress of ions-doped vanadate phosphors, including Eu3+, Sm3+, Dy3+, rare earth ions co-doped, and co-doped of alkali or alkaline earth metal ion and rare earth ion, were summarized. It is considered that the improvement of the preparation method can make the grain size of vanadate phosphors develop from micrometer to nanometer, which can be better used in the fields of lighting, displays, optical temperature sensors, color temperature indicators, etc. It is suggested that exploring vanadate substrates with different composition and crystal structure and the co-doped ions will be the main research direction in this field.
Keywords: vanadate; phosphor; rare earth ions; photoluminescence
中图分类号:TQ135.1
文献标志码:A
文章编号:1008-5548(2021)02-0102-09
DOI:10.13732/j.issn.1008-5548.2021.02.014
收稿日期: 2020-09-21, 修回日期:2020-10-06,在线出版时间:2020-12-22 16:32。
基金项目:四川省应用基础重点项目,编号:2019YJ0688。
第一作者简介:张磊(1994—),男,硕士研究生,助教,研究方向为钒酸盐发光材料的研究与开发。E-mail:836369815@qq.com。
通信作者简介:张雪峰(1965—),男,硕士,教授,硕士生导师,研究方向为钒钛功能材料。E-mail:532256335@qq.com。