Improvement of mechanical properties of waste glass powder composite mortar by autoclave curing

CHEN Cong, KE Guojun, TAN Tiange, ZOU Pinyu

(School of Civil Engineering,University of South China,Hengyang 421001,China)

Abstract: In order to improve the mechanical properties of glass powder composite mortar, the preparation method of autoclaved aerated brick was referred. The glass powder composite cement mortar was prepared by autoclaved curing with different proportion of waste glass powder instead of cement. The mechanical property changes of waste glass powder composite mortar were studied by diffraction of X-ray, scanning electron microscope and other experimental methods. The results show that under the standard curing, the strength of waste glass powder composite mortar decreases with the increasing of the replacement ratio, while under the autoclave curing, the strength of glass powder composite mortar changes in a convex shape with the increasing of the replacement ratio. With the optimal content of 30%, its 60 day strength exceeds 17.6% of the reference cement mortar. It is suggested that the replacement ratio of glass powder is 30% to prepare glass powder composite mortar.

Keywords: steam pressure maintenance;waste glass powder;mortar; mechanical properties

中图分类号:TU528.041                            文献标志码:A

文章编号:1008-5548(2020)04-0046-06

DOI:10.13732/j.issn.1008-5548.2020.04.008

收稿日期: 2020-01-10,修回日期:2020-02-25,在线出版时间:2020-05-09 16:39。

基金项目:湖南省自然科学基金项目,编号:2019JJ60003。

第一作者简介:陈聪(1994—),男,硕士研究生,研究方向为高性能混凝土及固体废渣利用。E-mail:458273342@qq.com。

通信作者简介:柯国军(1964—),男,教授,研究方向为高性能混凝土及固体废渣利用。E-mail:kegj320@sina.com。