WANG Xinghua1 a， WANG Ge1 a， WANG Haijian1 a，ZHU Yuying1 a， LI Qiang1 a， b，2
（1. a. National Engineering Research Center for Equipment and Technology of Cold Strip Rolling； b. National Key Laboratory of Metastable Materials Science and Technology， Yanshan University， Qinhuangdao 066004；2. College of Materials Science and Engineering， Hebei University of Science and Technology， Shijiazhuang 050018， China）
Abstract：Fe78-xMxSi13B9 soft magnetic amorphous alloy powders were prepared by high-energy ball-milling technology.Effects of the addition of transition metal elements M(Zr,Nb and Mo) on microstructure evolution,thermal stability and soft magnetic properties were analyzed by XRD,DSC,SEM and VSM.The results show that the addition of Zr and Nb are helpful to form amorphous phase in Fe-Si-B alloys.The maximum supercooled liquid region ΔTxis 70.62 K.The glass transition temperature Tg and the crystallization temperature Txare respectively 785.05 and 855.67 K.The saturation magnetization Msis 111 emu/g and the coercive force Hc is about 2 028.443 A/m.
Keywords：high-energy ball-milling;soft magnetic amorphous alloy;saturation magnetization
中图分类号：TG132.2+ 71 文献标志码：A
文章编号：1008-5548（2013）03-0039-04
DOI：10.3969/j.issn.1008-5548.2013.03.010
收稿日期：2012-11-24，修回日期：2012-12-12。
基 金 项 目 ： 河北省应用基础研究计划重点基础研究项目 ， 编 号 ：13961001D； 国家重点基础研究发展计划（973 计划）前期研究专项，编号：2009CB626603。
第一作者简介：王兴华（1985—），男，博士研究生，研究方向为非晶纳米晶合金制备技术与快速烧结技术。 E-mail：349427444@qq.com。
通信作者：李强（1962—），男，博士，教授，博士生导师，研究方向为非晶纳米晶合金粉末冶金制备技术。 电话：0335-8063946， E-mail：liqiang@ysu.edu.cn， liqiang@hebust.edu.cn。