Investigation on Surface Composite Modification of Flake Zinc Powders

YUE Gang, CAI Xiaolan, WANG Kaijun, HU Cui,YU Mingjun

(Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, China)

Abstract:The flake zinc powders were prepared by dry high energy ball milling. The orthogonal test was applied to investigate the effect of different additives formula on median particle size d50, apparent density and water surface covering of the milled flake zinc powders. The optimum formula of composite additives was identified. The results show that the best mass fractions of stearic acid, palmitic acid, zinc stearate and poly-ethylene glycol are 2.5%, 0.3%, 0.3% and 0.1%. The median particles size d50, apparent density and water surface covering was 13.12 μm, 0.934 8 g/cm3, 2 280.2 cm2/g. There is no new phase generated and the milled flake zinc powders are coated effectively.

Keywords:high energy ball milling; flake zinc powder; surface modification

中图分类号:TF813                    文献标志码:A

文章编号:1008-5548(2013)05-0080-04

DOI:10.3969/j.issn.1008-5548.2013.05.017

收稿日期:2013-02-18,修回日期:2013-03-01,在线出版时间:2013-10-25。

基金项目:云南省发改委科技计划项目,编号:1405141901。

第一作者简介:乐刚(1985—),男,硕士研究生,研究方向为金属复合材料与粉体工程。 电话:15911556573,E-mail:yuegang027@126.com。

通信作者简介:蔡晓兰(1965—),女,教授,博士生导师,研究方向为超细金属粉体与材料研究与设备开发。 E-mail:cxl9761@163.com。